Caracterização da deposição de pó cerâmico supercondutor de YBa2Cu3O7-d e SmBa2Cu3O7-d em aço inoxidável 316L
Nenhuma Miniatura disponível
Data
2019-03-15
Autores
Corteletti, Rodolpho Toniato
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal do Espírito Santo
Resumo
In this work, microstructures of superconducting ceramics deposited in 316L stainless steel base were produced and characterized. The objective was to develop a fault currente limiter and evaluate the metal / ceramic junction and to change the mechanical properties of the superconducting ceramics. Thus, for this purpose in mind, YBa2Cu3O7-d and SmBa2Cu3O7-d polycrystalline ceramics were prepared by conventional method from the solid-state reaction. In addition, the 316L stainless steel plates were cut into rectangular pieces of approximately 72 mm x 10 mm x 2.5 mm. The yttrium-based superconducting ceramics deposited in the steel were named sample A and samarium-based ceramics were named sample B. Each of the samples were thermally treated with different isotherms. Sample A was maintained at a plateau of 1040 ° C and sample B at a plateau of 1060 ° C, followed by cooling to 520 ° C for 24 hours. It is then cooled to room temperature. All thermal process was under oxygen flow with 99.9% purity. The characterization of these samples was performed by X-ray diffraction, optical microscopy, scanning electron microscopy and dispersive energy spectroscopy. The results indicate that the ceramics covered steel body, there are recrystallized signals and presented a boundary size of grain outline. We conclude that the composite preparation process was effective in the control of grain boundary size.
Descrição
Palavras-chave
Cerâmica , Supercondutividade , Aço inoxidável , Junção metal/cerâmica , Ceramic , Superconductivity , Stainless Steel , Metal/ceramic junction